A detailed investigation for the influence of post weld heat treatment （PWHT） on the microstructure of TC4 and TC17 dissimilar joints was analyzed. The fully transformed microstructure in the as-welded zone indicated that the peak temperature exceeded theβ-transus temperature at the weld interface during linear friction welding. TC4 side was mainly composed of martensiteα′phase with random distribution and it was singleβfor that of TC17. In the thermomechanically affected zones of TC4 and TC17, the structure undergoes severe plastic deformation and re-orientation, yet without altering the phase fractions. After PWHT, in the weld zone of TC4 alloy, the phase transformationα′→α＋βoccurred and the acicularαwas coarsened, which resulted in a decrease in hardness. In the weld zone of TC17 alloy, fineαphase precipitated at the grain boundary and withinβgrains, which resulted in a sharp increase in hardness.